A. Definition
The traditional definition: Refractory degree not lower than 1580 degrees Celsius inorganic non-metallic materials;
ISO definition: Refractory degree not lower than non metallic materials and products 1500 degrees Celsius.;
B. Classification
Common refractory: 1580 to 1770 DEG C
Advanced refractory materials: 1770 to 2000 DEG C
Special refractory material: >2000 C