company news about The damage reason of ladle refractory

Certification
China Zhengzhou Rongsheng Refractory Co., Ltd. certification
China Zhengzhou Rongsheng Refractory Co., Ltd. certification
Customer Reviews
Products have high quality&Service was outstandingly friendly and efficient

—— Aslam Baig (Pakistan)

The seller is very kind, thanks for recommending the right products for our cement kilns.

—— Santhosh Thomas

The sample meets our need, hope we can start our first order quickly.

—— Tanveer Ahmed

I'm Online Chat Now
Company News
The damage reason of ladle refractory

1. The chemical effect

1) The composition of molten steel erosion of refractories.

2) Erosion of slag composition on refractories.

3) At high temperatures, the damage caused by refractory material itself produces reaction, generate new minerals produced by the phase change volume effect brought by and under the action of vacuum volatilization and other reasons.

 

2.Physical effect

1) The scouring effect of refractory steel.

2) Heat shock steel repeated the role in refractory material cause, cause of refractory cracking and spalling.

3) Refractory its thermal expansion damage effect in favor of.

4) Fusion inhibition of molten steel for refractory material.

 

3. The artificial reason

1) And refractory material selection improper collocation.

2) Improper use of the refractories. Such as masonry, improper baking.

3) Ladle turnaround period is too long to cause cold pack.

4) Unpacking properly, damage the ladle backing layer.

5)Not take remedial measures.

Pub Time : 2015-01-12 09:39:05 >> News list
Contact Details
Zhengzhou Rongsheng Refractory Co., Ltd.

Contact Person: Mr. Pika

Tel: 86-13838387996

Fax: 86-0371-86555658

Send your inquiry directly to us (0 / 3000)