Product Details:
|
| Place Of Origin: | Henan, China | Shape: | Brick, Standard Or Customized By Your Drawings |
|---|---|---|---|
| Material: | Alumina Block | SiO2 Content (%): | - |
| Al2O3 Content (%): | 48%-85% | MgO Content (%): | 0.8-1.2 |
| CaO Content (%): | 0.34% | Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°) |
| CrO Content (%): | 0.1-0.3% | SiC Content (%): | 1.2-1.4 |
| Model Number: | High Alumina Brick | Fe2O3: | ≤2.5% |
| Dimension: | ISO Size | Crushing Strength: | 40~60 Mpa |
| Apparent Porosity: | ≤23% | ||
| High Light: | Blast Furnace High Alumina Brick,Fire Resistant High Alumina Brick,85% Al2O3 Refractory Brick |
||
Blast Furnace 85% Al2o3 High Alumina Brick For Fire Resistant
Product specifications
High alumina refractory is alumina silicate refractory with Al2O3 content above 48%.Generally divided into three categories, first class: the content of Al2O3 is greater than 75%;Second class: Al2O3 content 60% ~75%;Third grade: Al2O3 content 48% ~ 60%.It can also be classified according to its mineral composition.The proportion of each mineral phase depends on the type and quantity of Al2O3/SiO2 and the impurity contained in the product, and also on the production process conditions.
We bring forth high quality High Alumina Bricks, which is manufactured to meet the requirements of neutral refractoriness where safe working temperature is more than 1300 degree centigrade. We offer high Alumina Bricks in different specifications as per customer requirements.
Features
1. High refractoriness.
2. Good spalling resistance and wear resistance.
3. Good corrosion resistance.
4. Good thermal shock resistance.
5. High mechanical strength.
6. High-temperature creep rate is low.
Suitable For
Cement Rotary Kilns
Laddle Lining
Glass industries
Blast furnaces Stoves & Checkers
Electric Furnace Roof
Physical and chemical indexes
| High Alumina Brick | ||||||
| Item | Index | |||||
| LZ-48 | LZ-55 | LZ-65 | LZ-75 | LZ-80 | ||
| AL2O3 (≥%) | 48 | 55 | 65 | 75 | 80 | |
| Fe2O3 (≤%) | 2.0 | 2.0 | 2.0 | 2.0 | 1.8 | |
| Refractoriness Under Load (0.2Mpa)≥ ℃ | 1420 | 1450 | 1500 | 1520 | 1530 | |
| Reheating Linear Change | 1500℃*2h | – | 0.1-0.4 | 0.1-0.4 | 0.1-0.4 | 0.1-0.4 |
| 1450℃*2h | 0.1-0.4 | – | – | – | – | |
| Apparent Porosity (≤%) | 22 | 22 | 23 | 23 | 22 | |
| Cold Crushing Strength ≥ (MPa) | 35 | 40 | 45 | 50 | 55 | |
| Bulk Density (g/c m3) ≥ | – | – | – | – | – |
|