Product Details:
|
| SiO2: | ≤0.5% | Al2O3: | ≥77% |
|---|---|---|---|
| Fe2O3: | ≤0.5% | R2O: | ≤0.4% |
| S: | ≤0.1% | 325M Sieve Residue: | ≤5% |
| Initial Setting Time: | ≥45min | Final Setting Time: | ≤6h |
| Flexural Strength: | 1d ≥5.0MPa | Compressive Strength: | 1d ≥30MPa |
| High Light: | high temperature refractory cement,furnace refractory cement |
||
CA 80 Castable Refractory Cement Used in Machinery Processing , High Thermal Stability
Description:
The binding properties of aluminate cements are mainly due to the hydration of calcium aluminate.
Features:
1:Fast hard high strength
2:fire resistance
3:resistance to sulfate erosion
4.high refractoriness under load,
5. high thermal stability,
6.good creep resistance
7.thermal shock resistance.
Application:
metallurgy, petroleum, chemical industry, building materials, machinery processing, military, etc of thermal technology equipment.
| product | CA50F | A600 | A700 | A900 | CA50R | ||
|
Chemical Compositionn (%) |
SiO2 | ≤8.0 | ≤7.8 | ≤7.5 | ≤5.5 | ≤7.0 | |
| Al2O3 | ≥50.0 | ≥50.0 | ≥51.0 | ≥53.5 | ≥52.0 | ||
| Fe2O3 | ≤2.5 | ≤2.5 | ≤2.5 | ≤2.5 | ≤2.5 | ||
| R2O | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | ||
| S | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ||
| Cl | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ||
| 45µm residue (%) | ≤20 | ≤15 | ≤12 | ≤8 | ≤8 | ||
| Blaine (m2/kg) | ≥300 | ≥300 | ≥320 | ≥350 | ≥350 | ||
| InitialSetting (min) | ≥30 | ≥45 | ≥60 | ≥90 | ≥30 | ||
| FinalSetting (h) | ≤6 | ≤6 | ≤6 | ≤6 | ≤6 | ||
| Flexural strength (MPa) | 6h | —— | —— | —— | —— | ≥3.0 | |
| 1d | ≥5.5 | ≥6.0 | ≥6.5 | ≥8.0 | ≥7.0 | ||
| 3d | ≥6.5 | ≥7.0 | ≥7.5 | ≥10.0 | ≥8.0 | ||
| Compressive strength (MPa) | 6h | —— | —— | —— | —— | ≥30 | |
| 1d | ≥40 | ≥45 | ≥55 | ≥72 | ≥60 | ||
| 3d | ≥50 | ≥55 | ≥65 | ≥82 | ≥70 | ||