Product Details:
|
| Material: | Alumina, Carbon, Zircon | Refractoriness (℃): | 1770< Refractoriness< 2000 |
|---|---|---|---|
| Shape: | Plate | MOQ: | Negotiable |
| Quality: | Excellent | Type: | Refractory Material |
| Price: | Competitive | HS Code: | 69022000 |
| Lead Time: | Timely,on Time | ||
| High Light: | dry pressed Brick,Magnesia Carbon Bricks |
||
High Performance Slide Gate Plate For Ladle, Hot Selling High Quality In Manufacturer RS
Description:
Import metal or alloy into sliding plate, under middle temperature treatment, forms metal binding phase, and convert non-oxide binding phase when burnt on high temperature condition, therefore improves sliding plate's strength, thermal shock resistance and oxidation resistance, acceptable for different steel ladles, steel making plants.
Application:
The slide gate plate is used in the process of steel casting, widely used in large ladle, middle ladle and small ladle.
Features:
Excellent thermal shock resistance
High strength at high temperature,
Excellent resistance to erosion
Good resistance to rushing scour.
Low rough degree after slide surface is used
Low fissure expansion coefficient
Physical And Chemical Indicators For High Performance Slide Gate Plate:
| Item | RS-HBZ-D | RS-HBZ-F1 | RS-HBZ-M1 | RS-HBZ-F2 | |
| Chemical Composition (%) | Al2O3 % | 75 | 80 | 80 | 70 |
| MgO | -- | -- | -- | ||
| ZrO2 | -- | -- | -- | 5 | |
| C | ≤6 | ≤6 | ≤8 | 3 | |
| Density(g/cm3) | 3.00 | 3.05 | 2.95 | 3.00 | |
| apparent porosity % | 10 | 10 | 10 | 11 | |
| compression strength MPa | 100 | 120 | 100 | 95 | |
Physical And Chemical Indicators For High Temperature Firing Slide Gate Plate
| Item | RS-HBZ-A | RS-HBZ-B | RS-HBZ-C | RS-HBZ-D | |
| Chemical Composition (%) | Al2O3 % | 70 | 75 | 75 | 60 |
| MgO | -- | -- | 4 | -- | |
| ZrO2 | -- | -- | -- | 20 | |
| C | 4 | 4 | 4 | 4 | |
| Density(g/cm3) | 2.85 | 2.9 | 3.05 | 3.00 | |
| apparent porosity % | 6(10) | 6(10) | 6(10) | 6(10) | |
| compression strength MPa | 90 | 100 | 100 | 100 | |
Contact Person: Mr. Pika
Tel: 86-13838387996
Fax: 86-0371-86555658