Product Details:
|
| Material: | Magnesium Oxide (MgO) And Chromium Oxide (Cr2O3) | SiO2 Content (%): | 4.5-6.5% |
|---|---|---|---|
| Al2O3 Content (%): | 3.8-4.2% | MgO Content (%): | 65-80% |
| CaO Content (%): | 0.2-0.4% | CrO Content (%): | 7-17% |
| Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°), 1770°< Refractorines | SiC Content (%): | Little |
| Model Number: | Brick, Magnesite Chrome Brick | Brand Name: | Rongsheng |
| Apparent Porosity: | 17-18% | Applications: | Cement Rotary Kiln,glass Kiln Regenerative Chamber Etc |
Magnesia chrome brick is a kind of basic refractory material with more than 90% magnesium oxide content and periclase as the main crystal phase, and magnesia chrome brick has excellent features of high refractoriness, high temperature strength, good thermal shock resistance and strong basic slag erosion resistance. Magnesia chrome bricks are mainly used for steelmaking basic open hearth furnace, electric furnace bottom and wall, permanent lining of oxygen converter, non ferrous metal metallurgy furnace, high temperature tunnel kiln, lining of rotary kiln, furnace bottom and wall of heating furnace, regenerative chamber of glass furnace and so on.
Magnesite chrome block uses quality magnesia and chromic oxide as the raw material, molded through high press and fired in the high temperature. magnesia chrome bricks have features of large crystal and high direct bonding rate. and magnesite chrome fire bricks have good cracking resistance and good acid slag erosion resistance with low alkaline property. magnesite chrome block is the ideal lining brick material for finery out of furnace, electric furnace, glass furnace, melting furnace and rotary cement kiln.
.High flexibility,
.Low thermal conductivity,
.High temperature strength,
.Good thermal shock resistance,
.Strong furnace slag erosion resistance.
Due to the quality of magnesia chrome bricks, magnesia chrome brick is divided into ordinary magnesia chrome brick, direct bonded magnesia chrome brick, semi bonded magnesia chrome brick, rebonded magnesia chrome brick and so on.
Magnesia chrome bricks are made of bonded common sintered material, and eliminate loose effect caused of the expansion when producing the spinel by the reaction of MgO and Cr2O3, Al2O3 or FeO. Moreover, there is also unburned magnesite chrome fire brick such as unburned magnesite chrome block is made of inorganic magnesia saline solution. and unburned magnesia chrome brick is simple and low cost. this kind of magnesia chrome brick has great thermal stability, but its high temperature strength is lower than burnt magnesia chrome brick.
| Magnesia Chrome Bricks | |||||||
| Item/Index | MGe-20 | MGe-16 | MGe-12 | MGe-8 | DBMK-A | DBMK-B | DBMK-C |
| MgO≥(%) | 40 | 45 | 55 | 60 | 80 | 80 | 80 |
| CR2O3≤(%) | 20 | 16 | 12 | 8 | 6-8 | 6-8 | 6-8 |
| SiO2≤(%) | — | — | — | — | 2.0 | 2.5 | 3.0 |
| Apparent Porosity≤(%) | 23 | 23 | 23 | 24 | 18 | 18 | 18 |
| Cold Crushing Strength≥(MPA) (15℃-25℃) | 24.5 | 24.5 | 24.5 | 24.5 | 40 | 40 | 40 |
| 0.2MPa Refractoriness Under Load ≥ (℃) | 1550 | 1550 | 1550 | 1530 | 1680 | 1650 | 1620 |
Application of Magnesia Chrome Bricks
Magnesia chrome brick is mainly used in metallurgical industry, such as building open hearth furnace, furnace top of electrical furnace, out of finery and all kinds of non ferrous smelting furnace. magnesite chrome block is also used in position of burning zone of rotary cement kiln and regenerative chamber of glass kiln.