Product Details:
|
| Place Of Origin:: | Henan, China | Shape:: | Brick |
|---|---|---|---|
| Material:: | Alumina Block | SiO2 Content (%):: | - |
| Al2O3 Content (%):: | 48%-85% | MgO Content (%):: | 0.8-1.2 |
| Refractoriness (Degree):: | Common(1580°< Refractoriness< 1770°) | SiC Content (%):: | 1.2-1.4 |
| Cold Crushing Strength(MPa):: | 40~70MPa | Color:: | Yellow |
| Certificate:: | ISO9001 | Keyword:: | Good Price High Alumina Refractory Brick For Furnace Lining |
| High Light: | Anti Corrosion High Alumina Refractory Brick,Furnace Lining High Alumina Refractory Brick,Furnace Lining High Alumina Fire Bricks |
||
Good price high alumina refractory brick for furnace lining
Product specifications
High alumina refractory is alumina silicate refractory with Al2O3 content above 48%.Generally divided into three categories.It can also be classified according to its mineral composition.The proportion of each mineral phase depends on the type and quantity of Al2O3/SiO2 and the impurity contained in the product, and also on the production process conditions.
We bring forth high quality High Alumina Bricks, which is manufactured to meet the requirements of neutral refractoriness where safe working temperature is more than 1300 degree centigrade. We offer high Alumina Bricks in different specifications as per customer requirements.
| Material | high alumina bauxite |
| Color | earthy yellow |
| Size | Standard sizing: 230 x 114 x 65 mm ,Special size and OEM Service also provide! |
| Shape | Straight Brick,special-shaped brick,checher brick,trapezoidal brick,Bricks with taper,arch brick,skew brick,ect. |
Features
1. High refractoriness.
2. Good spalling resistance and wear resistance.
3. Good corrosion resistance.
4. Good thermal shock resistance.
5. High mechanical strength.
6. High-temperature creep rate is low.
Suitable For
Cement Rotary Kilns
Laddle Lining
Glass industries
Blast furnaces Stoves & Checkers
Electric Furnace Roof
Physical and chemical indexes
| Item | Index | ||||
| International Code Name | SK35 | SK36 | SK37 | SK38 | SK40 |
| Chinese Code Name | LZ-48 | LZ-55 | LZ-65 | LZ-75 | LZ-80 |
| Al2O3,% | ≥48 | ≥55 | ≥65 | ≥75 | ≥80 |
| Fe2O3,% | ≤2 | ≤2 | ≤2 | ≤2 | ≤2 |
| Refractoriness℃,min | 1750 | 1770 | 1790 | 1790 | 1790 |
| Apparent Porosity,% | ≤22 | ≤22 | ≤23 | ≤23 | ≤21 |
| Bulk Density,g/cm3 | 2.25-2.35 | 2.25-2.35 | 2.25-2.35 | 2.25-2.35 | 2.25-2.35 |
| Cold Crushing Strength Mpa | ≥39 | ≥44 | ≥49 | ≥54 | ≥65 |
| 0.2Mpa Refractoriness Under Load T0.2 ℃,min | ≥1420 | ≥1470 | ≥1500 | ≥1520 | ≥1530 |