Definition of Silicon Manganese Nitride:
Silicon manganese nitride is mainly composed of S3N4 and Mn5N2. Accompanied by a mixture of non-silicon iron nitride, non-silicon manganese and a small amount of other ingredients. The granular product of silicon manganese nitride is off-white.
The Main Components of Silicon Manganese Nitride:
The median value of N is taken as 28%, the median value of Si is taken as 41.5%, 3% of the binder and aeration. Therefore, the basic ingredients (%) of the silicon manganese synthesis raw materials are: Si: 60. 1%, Mn ≦ 21. 7%, Fe ≦ 18.8%.
According to empirical data of large-scale industrial production, the conversion rate of Si to Si3N4 is generally 90 ~ 100%, and the maximum amount of Mn combined nitrogen is 9%. The main components of silicon manganese nitride are calculated as follows:
N | Si | Mn | Fe |
26.9 ~ 28.9 | 42.7 ~ 41.5 | 15.4 ~ 15.0 | 13.4 ~ 13.0 |
Considering the differences in the ingredients of different manufacturers and the differences in conversion rates, the FeMnSiN-A, FeMnSiN-B silicon content is set to 38.0 to 43.0, the nitrogen content is set to 26.0 to 30.0, and the manganese content is set to 10.0 to 15.0. FeMnSiN-C is relaxed on the basis of the above two grades and is an entry-level product for the production of silicon manganese nitride. The iron element in the product is not specified. For steelmaking, iron is a beneficial element, which is expressed in the standard as "surplus".
Parameter Index of Silicon Manganese Nitride:
Items | Mn | Si | N | C | S | P | Fe |
Ⅰ | 40~45 | 20~26 | 16~21 | ≤2.0 | ≤0.04 | ≤0.04 | surplus |
Ⅱ | ≤10 | 42~48 | 24~27 | ≤1.5 | ≤0.02 | ≤0.1 | |
Ⅲ | ≤15 | 38~45 | 25~30 | ≤0.8 | ≤0.02 | ≤0.1 | |
Granularity: 10~100mm |
Application of Silicon Manganese Nitride:
Silicon manganese nitride is mainly used as a nitrogenating agent for oriented silicon steel, as a nitrogenating agent for high-strength steels (such as HRB400), and also as a nitrogenating agent for casting.
Nitrogen is a strong element that forms and stabilizes austenite, and plays an important role in the solid solution and precipitation of carbonitrides in microalloyed steels.