Modulus Of Rupture:1.5MPa
Working Temperature:1450℃
Compressive Strength:≥50MPa
Working Temperature:High
Acid Resistance:High
Size:230x114x65 mm
Al2O3 Content (%):48%-85%
MgO Content (%):0.8-1.2
CaO Content (%):0.34%
Density:High
Chemical Stability:High
Linear Change:≤0.2%
Cold Crushing Stren:45-80
Thermal Shock Resistance:≥ 15 times
Volume Density:≥2.20g/cm3
Keyword:55% Al2O3 high alumina brick
Impact Resistance:High
Cold Crushing Stren:35-45
Refractoriness:≥1790℃
Application:High temperature industrial furnaces
Extended Kiln Life:Yes
Apparent Porosity:15-25%
Heat Resistance:High
Packing:Carton Box
Al2O3 Content (%):48%-85%
MgO Content (%):0.8-1.2
CaO Content (%):0.34%
Density:2.2-2.4g/cm3
Material:High Alumina
Oem:YES
Al2O3 Content (%):48%-85%
MgO Content (%):0.8-1.2
CaO Content (%):0.34%
Material:Alumina Block
SiO2 Content (%):-
Al2O3 Content (%):48%-85%