Product Details:
|
| Installation Method: | Vibration Casting | Abrasion Resistance: | Excellent |
|---|---|---|---|
| Water Addition: | 6-8% | Compressive Strength: | 20 Mpa |
| Volume Density: | 2.6 | Curing Method: | Air Setting |
| Type: | Low Cement Castable | Appliction: | Tundish Lining |
| Bending Strength Mpa: | 8~20 | Origin: | China |
| Oem: | Yes | Working Temperature: | 1800℃ |
| Thermal Conductivity: | 3 W/mK | Castable Color: | Gray |
| Color: | Light Grey | ||
| Highlight: | High Temperature Kiln Castable,Explosion-Proof Castable,Quick Drying Kiln Castable |
||
Low Cement Castable
LCC&ULCC refractory castable have the characteristics of small porosity, high density, good volume stability, high strength and small water addition. At the same time, LCC&ULCC overcomes the characteristics of the common castable that the strength of the castable decreases significantly at 800~1200℃, strength of LCC&ULCC increases with the increase of temperature. What is more, it has excellent thermal shock resistance, slag resistance and corrosion resistance.
Low Cement Refractory Castable Characteristics:
High temperature resistance 1800 degrees
High intensity
Excellent thermal shock resistance
Good corrosion resistance
Easy use when construction
| Item | Specification | |||
| Clay | High Alumina | Corundum | ||
| Al2O3 % | ≥45 | ≥75 | ≥98 | |
| CaO % | <1.8 | <1.5 | <1.0 | |
| Bulk Density, g/cm3 | 110℃×24h | ≥2.3 | ≥2.6 | ≥3.1 |
| 1350℃×3h | ≥2.26 | ≥2.61 | / | |
| 1550℃×3h | / | / | ≥3.00 | |
| CCS, MPa | 110℃×24h | ≥70 | ≥75 | ≥85 |
| 1350℃×3h | ≥85 | ≥90 | / | |
| 1550℃×3h | / | / | ≥100 | |
| CMOR, MPa | 110℃×24h | ≥6 | ≥8 | ≥9 |
| 1350℃×3h | ≥8 | ≥9 | / | |
| 1550℃×3h | / | / | ≥11 | |
| PLC, % | 1000℃×3h | -0.3 | -0.2 | -0.2 |
| 1350℃×3h | ±0.3 | ±0.5 | / | |
| 1550℃×3h | / | / | ±0.5 | |
| Max Working Temperature, ℃ | 1450 | 1600 | 1800 | |