Product Details:
|
| Al2O3: | 40% | ZrO2: | 34% |
|---|---|---|---|
| SiO2: | 14% | Na2O: | 1.6% |
| Bulk Density: | 3.95g/cm3 | Certificate: | CE |
| Origin: | China | ||
| Highlight: | kiln fire brick,building bricks |
||
AZS 33 Zirconia Corudum Bricks For Glass Furnace
Future
1.Casted by melting raw material in the mold, then cooling and solidification.
2.Strong glass corrosion resistance and high thermal shack stability.
3. High-purity raw material, barely no pollution.
4.Good wear-resistance,dregs-resistance and alkali corrosion resistance.
5.Top quality, long service time.
Specification
| Reference Index | AZS-33# | AZS-36# | AZS-41# | |
| Chemical Composition | Al2O3 | — | — | — |
| ZrO2 | 32-34% | 35-37% | 40-42% | |
| SiO2 | ≤16.0% | ≤14% | ≤13.0% | |
| Na2O | ≤1.5% | ≤1.6% | ≤1.3% | |
| Fe2O3+TiO2+CaO +Ma2O+K2O+B2O3 |
≤2.5% | ≤2.5% | ≤2.5% | |
| Bulk density( Dense part) | 3.85g/cm3 | 3.95g/cm3 | 4.0g/cm3 | |
| Corrosion resistance of glass melt (common glass,1500℃*36h) |
≤1.6mm/24h | ≤1.5mm/24h | ≤1.3mm/24h | |
| Bubbling separate (common glass,1300℃*10h) |
≤2.0% | ≤1.5% | ≤1.3% | |