Product Details:
|
| Carbon Content: | 99% | Apparent Porosity: | 8-10% |
|---|---|---|---|
| Bulk Density,g/Cm3: | 1.6 | Ash Content,%: | 8 |
| Compressive Strength,Mpa: | 68 | Flexural Strength,Mpa: | 26.9 |
| High Light: | heat resistant bricks,cement kiln bricks |
||
99% Impregnated Graphite Kiln Refractory Bricks , Anticorrosive Carbon Brick
The impregnated graphite carbon brick produced by the high-quality graphite carbon material, adding organic compounds with strong acid resistance. It is refined by high pressure molding, vacuum impregnation and high temperature heat treatment process. It has excellent acid and temperature resistance. It is an ideal lining material for phosphoric acid reaction tank and phosphoric acid storage tank in chemical industry.
The impregnated graphite carbon brick has the following characteristics:
1, Excellent corrosion resistance
Product used the graphite carbon material with excellent acid resistance, adding strong organic compound, effective reduce the product porosity, increases the bulk density of the products, and thus the product has excellent anti-corrosion performance and strong wear resistance.
2 ,Stable performance and strong durability
The product adopts high strength organic adhesive as binder and bring high and new technology additive, so the product has strong strength, good abrasion resistance, very stable structure, and the structure of product does not change with the change of temperature.
3, Accurate size
It adopts pressing molding, the quality of the product is good, the dimension of the product is accurate, and the special product can be produced according to the requirements of the user.
Index of Impregnated graphite carbon brick
| Item | Units | Result |
| Carbon Content | % | 99% |
| Apparent porosity | % | 8-10 |
| Bulk density | g/Cm3 | 1.6 |
| Ash Content | % | 8 |
| Compressive strength | Mpa | 68 |
| Flexural Strength | Mpa | 26.9 |
| Roasting shrinkage at 800 ºC | No Change | |
| Thermal Conductivity | W/M.K | 5.1@200ºC |