Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee

Name: Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee
Brand: Zhengzhou Rongsheng Refractory Co., Ltd.
Price: 15,000.00 USD
Availability: InStock

All Products

Kiln Refractory Bricks
(134)

Refractory Fire Bricks
(36)

High Alumina Refractory Brick
(127)

Micro Nano Insulation Material
(34)

Zirconium Silicate Ceramics
(18)

Fireclay Brick
(39)

Refractory Raw Materials
(14)

Silica Refractory Bricks
(44)

Magnesia Bricks
(69)

Corundum Brick
(40)

Insulating Fire Brick
(47)

Mullite Brick
(42)

Refractory Castable
(146)

Refractory Products
(59)

Ceramic Fiber Blanket
(55)

Furnace Bricks
(19)

Fireplace Refractory Brick
(14)

Graphite Electrode
(31)

Best Products

$The Hot-Selling And Customized Size Magnesite Chrome Refracotry Brick For Glass Kiln Furnace$

The Hot-Selling And Customized Size Magnesite Chrome Refracotry Brick For Glass Kiln Furnace

$Good Creep Resistance Kiln Refractory Low Porosity Small Fire Bricks Andalusite Brick As The Lining And Checker$

Good Creep Resistance Kiln Refractory Low Porosity Small Fire Bricks Andalusite Brick As The Lining And Checker

$Dry Pressed Kiln Refractory Bricks$

Dry Pressed Kiln Refractory Bricks

Customer Reviews

Products have high quality&Service was outstandingly friendly and efficient

—— Aslam Baig (Pakistan)

The seller is very kind, thanks for recommending the right products for our cement kilns.

—— Santhosh Thomas

The sample meets our need, hope we can start our first order quickly.

—— Tanveer Ahmed

I'm Online Chat Now

Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee

$Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee$ $Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee$

$Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee$

Large Image : Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee

Product Details:

Place of Origin:	Henan, China
Brand Name:	RONGSHENG
Certification:	ISO9001

Payment & Shipping Terms:

Minimum Order Quantity:	1 Ton

Contact Now

Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee

Description

Chemical Composition:	Al2O3-SiO2	Thermal Conductivity (W/M·K):	1.3-1.5
Carbon Content:	99%	Raw Materials:	Phosphate
Cold Crushing Strength (Mpa):	20-40	Refractoriness Under Load:	Min 1620°C
Fe2O3 Content (%):	1.5-2.5	Standard Size:	Customized Size
Apparent Porosity (%):	18-26	Oem Odm:	Acceptable
Density:	2.3g/cm3	Transportation:	Shipping
Working Temperature:	1450℃	Use:	Lime Kiln And Other Kiln Project
Bulk Density:	0.9g/cm3
Highlight:	Sintered Magnesite Brick , Magnesium Refractory Bricks , 95% Mgo Fused Magnesite Brick

Product Description

$Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee 0$

Magnesite Brick Introduction Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750℃. They are ideal products for glass furnace application. 

Magnesia Bricks generally can be classified into two types of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. 1. Burnt Magnesia Bricks have high purity and firing temperature as the direct contact with periclase crystalline grain. 2. Chemical bonded magnesite brick is made of fused magnesite as the raw material. Magnesium Refractory Bricks Specifications Rongsheng MGO contents range from 85% to 98% Widely used throughout metallurgical industry

$Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee 1$

Features

Magnesium Refractory Bricks Features1.High refractoriness, usually the refractoriness is above 2000°C. 2.Strong ability to resist basic (alkaline) slag, can not contact with acid refractory material. 3.Strong ability of thermal conductivity, sometime need insulating material. 4.Excellent resistance in slag abrasion,Higher bulk density 5.Lower apparent porosity and Lower impurity content

$Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee 2$

$Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee 3$

Specification

Rongsheng Refractory Magnesia Brick Technical Data:

Brand	MZ-92	MZ-95	MZ-97	MZ-98
MgO % ≥	92	95	97	98
CaO % ≤	2	1.7	1.3	1.2
SiO2 % ≤	1.2	1	0.7	0.6
Fe2O3 % ≤	1.2	1	0.8	0.5
Bulk Density≥ g/cm3	2.9	2.95	2.95	3
A.P. % ≤	16	16	16	15
C.C.S (Mpa) ≥	60	70	70	80
0.2mpa Refractoriness under load T0.6 ≥ °C	1530	1650	1700	1700

Shapes &Sizes of Rongsheng Magnesite Refractory Brick:

Straight	Split	Arch	Wedge	Tile	Other Shape
L×W×H(mm)	L×W×H (mm)	L×W×H/h(mm)	L×W×H/h (mm)	L×W×H (mm)	Key brick,
230×114×65	230×114×25	230×114×65/45	230×114×65/45	230×230×38	Skew brick,
230×114×75	230×114×32	230×114×65/55	230×114×65/55	230×230×50	Soap,
	230×114×37	230×114×75/45	220×114×75/45	230×230×65	Checker,
	230×114×50	230×114×75/55	220×114×75/55	230×230×75	Neck,
		230×114×75/65	220×114×75/65		Taper,
We also can make brick according to customers' drawing and requirements.