Product Details:
|
| Cold Crushing Strength: | ≥35MPa | Chemical Resistance: | Excellent |
|---|---|---|---|
| Bulk Density Dried: | ≥2500 | Cold Compressive St: | Min 100 |
| Aluminum Content: | ≥75% | Apparent Orosity: | ≤22% |
| Compressivestrength: | ≥ 50 MPa | Sizedimensions: | 230 X 114 X 65 Mm (standard) |
| Color: | Red, White, Gray, Or Brown Depending On Material | Keyword: | Low Porosity Fire Clay Brick |
| Modulus Of Rupture: | 1.5MPa | Thermal Conductivity: | 1.5W/m·K |
| Using Temperture: | 800℃ | Chemical Composition: | SiO2, Al2O3, Fe2O3 |
| Ash: | 0.3% | ||
| Highlight: | high strength refractory clay brick,fire resistant kiln fire bricks,industrial furnace lining bricks |
||
ire Clay Brick Introduction
Fire clay brick is made of local top grade fireclay materials under the high temperature according to the lasted national standard, which possesses even bulk density, high strength, low thermal conductivity and low impurity. Fire clay refractory brick has wide usage and the largest production.
We bring forth high quality fire clay Bricks, which is manufactured to meet the requirements of neutral refractoriness where safe working temperature is more than 1500 degree centigrade. We offer fire clay Bricks in different specifications as per customer requirements.
Fire Clay Brick Features
1. Good performance in high temp refractoriness under load
2. Lower thermal line expansion in high temp
3. Lower impurity content
4. Good thermal shock resistance performance
5. Excellent resistance in slag abrasion
Good cold crush strength
| Fireclay Brick Alumina contents range from 35% to 48% Widely used throughout metallurgical industry |
|
| Material | fire clay material |
| Color | yellow fire brick |
| Size | Standard sizing: 230 x 114 x 65 mm ,Special size and OEM Service also provide! |
| Shape | Straight Brick,special-shaped brick,checher brick,trapezoidal brick,Bricks with taper,arch brick,skew brick,ect. |